HD Patina Removal Tip
I had a bad experience using Bar Keeper's Friend on my HDs recently: my mix was too concentrated and I left it on too long (although still only 1-3 minutes).
The result was that my blades looked even worse afterward and - in confirmation of so much we discuss on the forum - they started to cut poorly! The "micro-etching" of the solvent was enough that the steel started to "stick" more in food on the blade side, as you often experience with some "normal" patinas on iron from time to time. Today, in cutting a cantaloupe with my all-time favorite cantaloupe knife (my 210 Wa HD), I ran out of patience: rather than effortlessly gliding through the flesh, I could feel the drag on the steel—it had nothing to do with sharpness, and everything to do with an HD patina.
Well, I've tried touching up my HDs before using various methods, but none have worked exceptionally well. This time, I went all-out with one blade first, and the results were so good I treated all three. Here's what I did, using SANDPAPER:
600 grit with water, about 2 minutes per side.
1000 grit dry, about 2 minutes per side.
2000 grit dry, about 2 minutes per side.
In less than a half hour, my HDs look better than they have in several years! And, if anything, the finish essentially looks factory, not "sandpapered."
Just wanted to share the simplicity and excitement.
240 HD (bad picture, but accentuates high-grit thinning experiment marks as well as 6-year old citrus stain which looks like a water stain):
210 HD picture with BKF effects accentuated by some use of meats:
After sanding:
240mm is in the middle. 6-year old citrus patina is essentially gone!
The result was that my blades looked even worse afterward and - in confirmation of so much we discuss on the forum - they started to cut poorly! The "micro-etching" of the solvent was enough that the steel started to "stick" more in food on the blade side, as you often experience with some "normal" patinas on iron from time to time. Today, in cutting a cantaloupe with my all-time favorite cantaloupe knife (my 210 Wa HD), I ran out of patience: rather than effortlessly gliding through the flesh, I could feel the drag on the steel—it had nothing to do with sharpness, and everything to do with an HD patina.
Well, I've tried touching up my HDs before using various methods, but none have worked exceptionally well. This time, I went all-out with one blade first, and the results were so good I treated all three. Here's what I did, using SANDPAPER:
600 grit with water, about 2 minutes per side.
1000 grit dry, about 2 minutes per side.
2000 grit dry, about 2 minutes per side.
In less than a half hour, my HDs look better than they have in several years! And, if anything, the finish essentially looks factory, not "sandpapered."
Just wanted to share the simplicity and excitement.
240 HD (bad picture, but accentuates high-grit thinning experiment marks as well as 6-year old citrus stain which looks like a water stain):
210 HD picture with BKF effects accentuated by some use of meats:
After sanding:
240mm is in the middle. 6-year old citrus patina is essentially gone!
~J
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
-
- Posts: 3723
- Joined: Thu Jan 26, 2017 9:27 pm
- Location: British Columbia, Canada
- Has thanked: 213 times
- Been thanked: 551 times
Re: HD Patina Removal Tip
Thanks! It seems simple and effective. In using one of the knives tonight, I did notice that going to 2000 grit did leave some hairline scratches upon closer examination. As you can see in the photo, these are not obvious, not do they really change the "factory finish," if you want to call it that. But I figured I should point it out for those concerned.
~J
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
-
- Posts: 2359
- Joined: Thu Feb 22, 2018 8:37 am
- Location: Taylor, Az
- Has thanked: 185 times
- Been thanked: 142 times
Re: HD Patina Removal Tip
Thanks for sharing this. I was just wondering what to do on a knife I recently purchased that is in need of the same treatment. Nice post!
“The goal is to die with memories, not dreams.”
- Jeff B
- Posts: 14757
- Joined: Fri Jan 27, 2017 5:59 pm
- Location: Louisville, Kentucky
- Has thanked: 1987 times
- Been thanked: 2352 times
Re: HD Patina Removal Tip
Damn, now I have several knives to refinish....
Thanks for sharing that Joe, those look fantastic! I've used Flitz a lot with good results but I'd love to get back to that "new" look on a few of mine.
Thanks for sharing that Joe, those look fantastic! I've used Flitz a lot with good results but I'd love to get back to that "new" look on a few of mine.
If God wanted me to be a vegetarian he wouldn't have made animals taste so good.
Re: HD Patina Removal Tip
Joe, I’m assuming you did this by hand and not a belt grinder? From a past experience, when I use sand paper by hand, my scratch pattern is always curved. Is that the hairline scratches that you’re referring to?salemj wrote: ↑Thu Jun 28, 2018 9:29 pm Thanks! It seems simple and effective. In using one of the knives tonight, I did notice that going to 2000 grit did leave some hairline scratches upon closer examination. As you can see in the photo, these are not obvious, not do they really change the "factory finish," if you want to call it that. But I figured I should point it out for those concerned.
-- Garrick
Re: HD Patina Removal Tip
Those do look nice. I wouldn't be surprised if the scratches you see are the 600 grit scratches writ large and made clearer by polishing the area around them. If they really are 2000 grit scratches you could pull them off by dropping back to he 1000 grit or 600 grit paper and doing one or two very precise draws along the factory finish marks a la the Aaron Gough demo.
-
- Posts: 3723
- Joined: Thu Jan 26, 2017 9:27 pm
- Location: British Columbia, Canada
- Has thanked: 213 times
- Been thanked: 551 times
Re: HD Patina Removal Tip
Yes, that's exactly right. One of the blades had a bit more treatment because it was the "test" blade, and I noticed at least one side of that blade had some slight curves to some of the hairline scratches that allowed them to stand out just a bit. I'll check the other blades and see if I can get pictures to highlight it. As you can see from above, unless you are worried about "resale" or something, the scratches don't really change the overall aesthetics of the knife or the original look (the vertical hairline-like finish is definitely still dominant), and I'm sure spending more than just 2 minutes a side and using some kind of paper holder or backing (or using a belt) would keep everything in top shape. For me, this was just having some fun with a little experiment on some knives that I love, hence the title of "patina removal' rather than "refinishing." Haha.slobound wrote: ↑Fri Jun 29, 2018 1:29 amJoe, I’m assuming you did this by hand and not a belt grinder? From a past experience, when I use sand paper by hand, my scratch pattern is always curved. Is that the hairline scratches that you’re referring to?salemj wrote: ↑Thu Jun 28, 2018 9:29 pm Thanks! It seems simple and effective. In using one of the knives tonight, I did notice that going to 2000 grit did leave some hairline scratches upon closer examination. As you can see in the photo, these are not obvious, not do they really change the "factory finish," if you want to call it that. But I figured I should point it out for those concerned.
~J
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
Re: HD Patina Removal Tip
Completely agreed! I figure if it’s a knife I’m using, there’s no reason to worry about making it look like a museum piece.salemj wrote: ↑Fri Jun 29, 2018 9:07 amYes, that's exactly right. One of the blades had a bit more treatment because it was the "test" blade, and I noticed at least one side of that blade had some slight curves to some of the hairline scratches that allowed them to stand out just a bit. I'll check the other blades and see if I can get pictures to highlight it. As you can see from above, unless you are worried about "resale" or something, the scratches don't really change the overall aesthetics of the knife or the original look (the vertical hairline-like finish is definitely still dominant), and I'm sure spending more than just 2 minutes a side and using some kind of paper holder or backing (or using a belt) would keep everything in top shape. For me, this was just having some fun with a little experiment on some knives that I love, hence the title of "patina removal' rather than "refinishing." Haha.slobound wrote: ↑Fri Jun 29, 2018 1:29 amJoe, I’m assuming you did this by hand and not a belt grinder? From a past experience, when I use sand paper by hand, my scratch pattern is always curved. Is that the hairline scratches that you’re referring to?salemj wrote: ↑Thu Jun 28, 2018 9:29 pm Thanks! It seems simple and effective. In using one of the knives tonight, I did notice that going to 2000 grit did leave some hairline scratches upon closer examination. As you can see in the photo, these are not obvious, not do they really change the "factory finish," if you want to call it that. But I figured I should point it out for those concerned.
-- Garrick
-
- Posts: 3723
- Joined: Thu Jan 26, 2017 9:27 pm
- Location: British Columbia, Canada
- Has thanked: 213 times
- Been thanked: 551 times
Re: HD Patina Removal Tip
Ok, gotta protect my reputation...
When I say "minor scratches" that I didn't notice at first and that the original finish is "preserved," this is what I mean. Seriously—I cannot see the scratches in these images. I think I saw them yesterday under just the right lighting, and immediately after washing a blade, so maybe it was the water that brought them out. Regardless: YES, sandpaper will scratch, but "no," I don't think 2 mins per side starting with a wet 600 paper and using only two more progressions (1k and 2k) results in a "bad" finish for regular use!
These pictures show a variety of angles, shadows, and focus on all three knives:
When I say "minor scratches" that I didn't notice at first and that the original finish is "preserved," this is what I mean. Seriously—I cannot see the scratches in these images. I think I saw them yesterday under just the right lighting, and immediately after washing a blade, so maybe it was the water that brought them out. Regardless: YES, sandpaper will scratch, but "no," I don't think 2 mins per side starting with a wet 600 paper and using only two more progressions (1k and 2k) results in a "bad" finish for regular use!
These pictures show a variety of angles, shadows, and focus on all three knives:
~J
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
- Jeff B
- Posts: 14757
- Joined: Fri Jan 27, 2017 5:59 pm
- Location: Louisville, Kentucky
- Has thanked: 1987 times
- Been thanked: 2352 times
Re: HD Patina Removal Tip
Well from the pictures the finish looks excellent! Beyond acceptable by my standards thow mine might not be the highest.
Very well done Joe.
Very well done Joe.
If God wanted me to be a vegetarian he wouldn't have made animals taste so good.
- pd7077
- Posts: 1045
- Joined: Thu Feb 02, 2017 7:02 pm
- Location: Bay Area, CA
- Has thanked: 66 times
- Been thanked: 106 times
Re: HD Patina Removal Tip
If you wanna clean up the patina while sparing the original grind marks, then try using some diamond paste or emulsion. Just apply it on one of the hard felt blocks that Mark carries.
--- Steve
-
- Posts: 3723
- Joined: Thu Jan 26, 2017 9:27 pm
- Location: British Columbia, Canada
- Has thanked: 213 times
- Been thanked: 551 times
Re: HD Patina Removal Tip
Thanks for the tip! All things I don't have. If I invested in some diamond paste for this purpose, what kind/grit would you suggest?
~J
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
- Jeff B
- Posts: 14757
- Joined: Fri Jan 27, 2017 5:59 pm
- Location: Louisville, Kentucky
- Has thanked: 1987 times
- Been thanked: 2352 times
Re: HD Patina Removal Tip
Very good tip, thanks Steve. Just happen to have that stuff here too.
If God wanted me to be a vegetarian he wouldn't have made animals taste so good.
- pd7077
- Posts: 1045
- Joined: Thu Feb 02, 2017 7:02 pm
- Location: Bay Area, CA
- Has thanked: 66 times
- Been thanked: 106 times
Re: HD Patina Removal Tip
For a deeply set patina on a knife that has relatively pronounced grind marks, I usually go with a 6um emulsion. Those particles are large enough to get the job done quickly (3-5min) while still fine enough to not affect the original grind marks. If you’re cleaning up a knife with a high degree of polish, I would typically drop down to 1um.
One thing I noticed is that 6um and 3um are fine to use as pastes, but I don’t enjoy using pastes below that. They tend to feel too thick and are more difficult to work. I would suggest using a less viscout emulsion for 1um and finer. At present, all my diamond products are emulsions because I prefer to keep thing uniform. Damn OCD
--- Steve
- Kit Craft
- Posts: 4844
- Joined: Thu Jan 26, 2017 8:57 pm
- Location: Pennsylvania
- Been thanked: 11 times
Re: HD Patina Removal Tip
Cool tip, thanks for sharing. My HD2 shows zero patina/staining, as an aside. I was talking with Desol about that awhile ago, his is the same. I swear it is stainless. That 210 Yo HD is wicked, btw.
-
- Posts: 3723
- Joined: Thu Jan 26, 2017 9:27 pm
- Location: British Columbia, Canada
- Has thanked: 213 times
- Been thanked: 551 times
Re: HD Patina Removal Tip
Thanks. You should check out the SS version that Lepus is selling. I really, really, really want to buy it, but I just cannot justify it at this exact moment. It is probably an extremely close approximation of what the HD offers for most applications. I waited quite some time to snatch the 210 Yo. I really like it. It is a surprisingly different knife than the Wa version in the same length.
Every HD I own absolutely showed a patina from regular use alone. I didn't notice it at first, but over time, the change in color (to a darker grey) became more and more apparent when sharpening, if I remember correctly: the bevel went from being the same tone as the knife to slowly becoming more of a contrasting silver. Other aspects of the patina were mistakes (like the BKF, or the citrus stain, which happened shortly after I bought the 240 and my best friend used it to cut a lime while fixing me a drink and then didn't wash it...how could I ever be upset at a guy fixing me a drink?!?).
Perhaps in another couple of months you'll notice the bevel-colour thingy...maybe?!? In the meantime, it is hard to imagine it is not HD steel for at least one reason: Konosuke is increasingly frugal in their stamped kanji, so it is hard for those batches ever to get mixed up! haha.
~J
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
-
- Posts: 3723
- Joined: Thu Jan 26, 2017 9:27 pm
- Location: British Columbia, Canada
- Has thanked: 213 times
- Been thanked: 551 times
Re: HD Patina Removal Tip
Thanks, Steve. This is very helpful. I'm going to make a note of it as a potential add-on to a future order. Seems like something good to have around that will essentially last forever.pd7077 wrote: ↑Fri Jun 29, 2018 1:25 pm
For a deeply set patina on a knife that has relatively pronounced grind marks, I usually go with a 6um emulsion. Those particles are large enough to get the job done quickly (3-5min) while still fine enough to not affect the original grind marks. If you’re cleaning up a knife with a high degree of polish, I would typically drop down to 1um.
One thing I noticed is that 6um and 3um are fine to use as pastes, but I don’t enjoy using pastes below that. They tend to feel too thick and are more difficult to work. I would suggest using a less viscout emulsion for 1um and finer. At present, all my diamond products are emulsions because I prefer to keep thing uniform. Damn OCD
~J
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.
Comments: I'm short, a home cook, prefer lighter, thinner blades, and have tried dozens of brands over the years.